新型成型工艺结合PIP工艺制备SiC陶瓷

《新型成型工艺结合PIP工艺制备SiC陶瓷》由会员上传分享，免费在线阅读，更多相关内容在学术论文-天天文库。

1、分类号TB323学号14010035UDC密级公开工学硕士学位论文新型成型工艺结合PIP工艺制备SiC陶瓷硕士生姓名冉长春学科专业材料科学与工程研究方向陶瓷基复合材料指导教师周新贵教授国防科学技术大学研究生院二〇一六年十一月NewmodificationofmoldingprocesscombiningPIPprocessPreparationofSiCceramicsCandidate：RanChangchunAdvisor：ZhouXinguiAdissertationSubmittedin

2、partialfulfillmentoftherequirementsforthedegreeofMasterof（Engineering）inMaterialScienceandEngineeringGraduateSchoolofNationalUniversityofDefenseTechnologyChangsha，Hunan，P.R.China（November，2016）国防科学技术大学研究生院硕士学位论文目录表目录..................................

3、......................................................................................IV图目录..........................................................................................................................V摘要..................................

4、...............................................................................................iABSTRACT....................................................................................................................iii第一章绪论......................

5、............................................................................................11.1SiC陶瓷及其复合材料应用背景.....................................................................11.1.1在航空领域的应用........................................................

6、........................11.1.2在核领域的应用....................................................................................31.2碳化硅陶瓷制备工艺.......................................................................................41.2.1常规烧结工艺.................

7、.......................................................................51.2.2PIP工艺简介..........................................................................................71.2.3凝胶注模成型................................................................

8、........................81.2.4冷冻干燥成型......................................................................................121.3选题依据与研究内容.....................................................................................171.3.1选题依据..................