1、中国科技论文在线http://www.paper.edu.cnLi–La–Zr–O固态电解质包覆对富锂锰基层#状正极材料性能影响11112211,2**沈守宇，沈重亨，王琪，方俊川，苏航，李君涛，黄令，孙世刚5（1.厦门大学化学化工学院，福建省厦门市，361005；2.厦门大学能源学院，福建省厦门市，361005）摘要：采用溶胶-凝胶法在富锂锰基正极材料Li1.188Ni0.198Co0.087Mn0.553O2(LMO)表面成功包覆上了Li–La–Zr–O（LLZO）固态电解质层。运用SEM、TEM、XRD、ICP-AES、EIS等技
2、术对LLZO包覆前后的材料进行了表征。恒流充放电测试得到2wt%LLZO包覆的富锂材料10(LMO@LLZO)在1C下循环450圈后人具有193mAh/g的容量，循环保持率为84.8%；而在相同条件下，未包覆的材料仅剩125.4mAh/g容量，循环保持率为54.1%。这主要是由于Li–La–Zr–O包覆层提高了富锂材料表面的稳定性，有效的抑制了副反应的发生。另外，2wt%LLZO的包覆层还能通过降低传荷阻抗来提高材料的倍率性能。关键词：锂离子电池；富锂锰基层状正极材料；固态电解质包覆；电化学性能。15中图分类号：TM912;O646文献
3、标志码：ASuperiorelectrochemicalperformanceofLi-richlayeredcathodematerialbycoatingLi–La–Zr–Osolidelectrolyte11112ShenShouyu,SHENChongheng,WANGQi,FANGJunchuan,SUHang,LI211,320Juntao,HUANGLing,SUNShigang(1.CollegeofChemistryandChemicalEngineering,XiamenUniversity,Fujian,36100
4、5,China;2.CollegeofEnergyandSchoolofEnergyResearch,XiamenUniversity,Fujian,361005,China;3.)Abstract:ALi–richMn–basedlayeredoxideLi1.188Ni0.198Co0.087Mn0.553O2(LMO)materialwas25successfullycoatedwithLi–La–Zr–Osolidelectrolyte(LLZO)bysol–gelprocess.BothLLZO–coatedLMOandpri
5、stinematerialswerecharacterizedbyx–raydiffraction(XRD),scanningelectronmicroscopy(SEM),transmissionelectronmicroscopy(TEM),inductivelycoupledplasma–atomicemissionspectrometry(ICP–AES)andelectrochemicalimpedancespectroscopy(EIS)toexploretheeffectofLLZOcoatinglayer.Galvano
6、staticcharge-dischargetestsindicatethatafter450cyclesat1C,30the2wt%LLZO-coatedLMOmaterial(LMO@LLZO)exhibitsasignificantcyclestabilityof193mAhg–1capacitywithacapacityretentionof84.8%comparedtotheLMOmaterialof125.4mAhg–1capacitywithacapacityretentionof54.1%.Thisisbecauseth
7、eLi–La–Zr–Ocoatinglayerimprovethesurfacestabilityandsuppressedsidereactions.Inaddition,the2wt%LLZOcoatinglayercouldalsoimprovetherateperformanceoftheelectrodebyobviouslyreducinginterfacial35charge–transferresistance.)Keywords:lithium-ionbattery;Li-richlayeredoxide;solide
8、lectrolytecoating;electrochemicalperformance0引言[1]40自从1991年索尼公司将锂离子商业化以来，可充放电的锂离子电池在可移动电子设备的能量储备上面起这重要的