1、第19卷第4期粉末冶金材料科学与工程2014年8月Vb1.19No.4MaterialsScienceandEngineeringofPowderMetallurgyAug.2014固溶处理工艺对压铸Mg.9AI-IZn一0.2Mn合金微观组织与硬度的影响肖代红,李秀秀,刘丹,陈亮(中南大学粉末冶金冶金国家重点实验室,长沙410083)摘要:采用不同的固溶处理工艺对冷室压铸法制备的Mg.9A1.1Zn一0.2Mn(质量分数)合金进行热处理,随后在150~C/5h条件下进行时效处理,通过X射线衍射、金相显微镜与扫描电镜观察及硬度
2、测试,研究固溶处理工艺与时效对合金显微组织与硬度的影响。结果表明,固溶处理可使压铸态合金晶界处的p.Mgl7A112相充分分解并溶入到ct-Mg基体中。提高固溶温度和延长固溶时间,均可减少以连续网状形态分布于Ct—Mg枝晶问的p-Mg17A112硬脆相,使其由晶间析出转变为0t.Mg晶内析出。但固溶温度过高或固溶时间过长都导致Ⅱ.Mg基体组织粗化,并发生过烧现象。固溶处理后的时效过程中,~-Mgl7A112相从过饱和固溶体中以不连续和连续2种方式析出,从而提高合金的硬度。关键词:压铸镁合金:固溶处理;显微组织;硬度中图分类号:
3、TG146.2文献标识码:A文章编号:1673.0224(2014)4.0570.06Effect0fsolid.solutiontreatmentonmicrostructureandhardnessofdie-castingMg-9AI-1Zn-0.2MnalloyX1AODai-hong,LIXiu—xiu,LIUDan,CHENLiang(StateKeyLaboratoryofPowderMetallurgy,CentralSouthUniversity,Changsha410083,China)Abstract:M
4、g一9AI-1Zn一0.2Mnalloy(massfraction,%)preparedbycoldchamberdiecastingwasheattreatedbydiferentsolutiontreatmenttechnologiesandthenagedat150℃/5h.Theefectofsolutiontreatmentonthemicrostructureandhardnessofthedie-castingalloyswasinvestigatedusingX—raydifraction,opticalmic
5、roscope,scanningelectronmicroscopyandVickershardnesstesting.Theresultsshowthatthe13-Mg17Al12phasesdistributedalongthegrainboundarycalldissolveinto0【一Mgmatrixthroughthesolid—solutiontreatment.Withincreasingtemperatureandtimeofsolid-solutiontreatment,the~-MgI7AII2phas
6、eexistedcontinuouslyasnetlikeinthegrainboundariesofct-Mgphasedecreasesandprecipitatesattheinnerof0【一Mgcrystalinsteadofingrainboundaries.However,thecrystalgrainofdie—castingalloywillbecoarsedandoversinteringifthesolutiontemperatureistoohilghorthesolutiontimeistoolong
7、.Theagingtreatmentaftersolid-solutiontreatmentmake3-Mg17A112phasesOccurwithdiscontinuousandcontinuousprecipitationfromoversaturateda-Mgsolidsolution,andthusincreasethehardnessofthedie—castingalloys.Keywords:die-castingmagnesiumalloys;solid-solutiontreatment;microstr
8、ucture;hardnessMg—A1.Zn系(AZ系镁合金具有密度低、比刚度易形成粗大的低熔点Mg1A112相,该相在高温下易软和比强度高、抗震、抗电磁干扰、以及制备工艺简单化和粗化l引。研究表明通过合金化、形变热处理或采等优点,广泛用于航空航天、汽车工业、以及计算机用粉