1、常用焊接结构用铸钢的化学成分及碳当量上限值标准牌号CMnSiPS残余元素碳当量NiCrCuMoV总量国际标准(ISO3755-1991)200~400W0.251.000.600.0350.0350.400.350.400.150.051.0 230~450W0.251.200.600.0350.0350.400.350.400.150.051.0 270~480W0.251.200.600.0350.0350.400.350.400.150.051.0 340~550W0.251.500.600.0350.0350.400.

2、350.400.150.051.0 我国标准(GB/T7659-1987)ZG200~400H0.200.800.500.040.040.300.300.300.150.050.80.38ZG230~450H0.221.200.500.040.040.300.300.300.150.050.80.43ZG270~485H0.251.200.500.040.040.300.300.300.150.050.80.45日本标准(JISG5102-1991)SCW4100.221.500.800.040.04      0.40SCW

3、4500.221.500.800.040.04      0.43SCW4800.221.500.800.040.040.500.50    0.45SCW5500.221.500.800.040.042.500.50 0.300.20 0.48SCW6200.221.500.800.040.042.500.50 0.300.20 0.50美国标准(ASTMA216-1998)WCA0.250.700.600.040.0450.500.400.500.250.031.00.50WCB0.301.000.600.040.0450

4、.500.400.500.250.031.00.50WCC0.251.200.600.040.0450.500.400.500.250.031.00.552/2焊接结构用铸钢的力学性能标准牌号σs/MPaσb/MPaδ(%)φ(%)冲击性能Akv/Jaku/(J/cm2)国际标准(ISO3755-1991)200~400W230~450W270~480W340~550W200230270340400~550450~600480~630550~700252218154031252145452220 我国标准(GB/T7659-1

5、987)ZG200~400HZG230~450HZG270~485H200230275400450485252220403535302522594424日本标准(JISG5102-1991)SCW410SCW450SCW480SCW550SCW6202352552753554304104504805506202120201817 2828282828 美国标准(ANSI/ASTMA216-1998)WCAWCBWCC205205275415~585485~655485~655242424353535  资讯来源:国家标准化管理

6、委员会2/2

当前文档最多预览五页,下载文档查看全文

此文档下载收益归作者所有

当前文档最多预览五页,下载文档查看全文
温馨提示:
1. 部分包含数学公式或PPT动画的文件,查看预览时可能会显示错乱或异常,文件下载后无此问题,请放心下载。
2. 本文档由用户上传,版权归属用户,天天文库负责整理代发布。如果您对本文档版权有争议请及时联系客服。
3. 下载前请仔细阅读文档内容,确认文档内容符合您的需求后进行下载,若出现内容与标题不符可向本站投诉处理。
4. 下载文档时可能由于网络波动等原因无法下载或下载错误,付费完成后未能成功下载的用户请联系客服处理。