1、摘要通过一系列的分析,制定相应的实验方案,确定以不同的合成方法,辅以⋯定的元素掺杂,制备压电陶瓷粉体。将陶瓷粉体与高分子聚合物PVDF复合,在一定温度和静电场下进行材料极化,制备压电复合材料样品。对不同方案所得复合材料样品进行性能测试表明,经过改良方案后获得材料的压电常数得到了一定程度的提高。关键词:复合模型,0.3复合,压电常数,介电常数,粒度,极化ll茎堡堡三丕鲎!壁主堂垡堡苎Despitetherearemanyinvestigationaroundpiezo-compositematerials,theobstaclestillstandsthere
2、thathowtoenhancethepiezoelectricpropertyofpiezo-composites.Inordertoworkoutthequestion,severalacademiccompositemodelsweresetupaccordingtosomeordinarylawsinthisthesis.sothatdatacanbeanalysistofindouttheoptimizingwaystoenhancethecharacteristicsofthematerial.Accordingtothesemodels,per
3、mittivity,piezoelectricity,Young’smoduleaswellasparticlesizeofthecomponentsaffectedthepiezoelectricityofcompositecommonly.Inordertoraisethepiezoelectricconstantofcomposite,manyaspectsshouldbepaidattentionto.Thepermittivityofcomponentdeterminedtheelectricdistributioninthecomposite,w
4、hichhelduptheelectricfieldwhilepolarizingthematerialorpushing/pullingthematerial.Accordingtonon-organ/organcomposite,sincetheorganparttookonlowerpermittivity,itinclinedtoholdonmostpotential,makingthepiezoelectricityofcompositedeteriorate.Thus,itissignificanttodiminishthepermittivit
5、yofceramicpowdersandtoemploypolymerswithhJ【ghdielectricconstantasthecomponentofpiezo-composite.Norcanfinepiezoelectricitybegainedwhileallcomponentspromptedhighpiezoelectricconstantinpiezo-composite.Thereisagreatdefectivethatthepiezoelectricconstantofceramicsandpolymersholdopposites
6、ymbolwhiletheyarepolarizedatsametime.Thereexist3routinetoovercomethedefective:(a)diminishingthepiezoelectricityofpolymers;Co)raisingthepiezoelectricityofceramicpowders;(c)employingtwicepolarizationprocessing,whichmakesthebothcomponentspromptpiezoelectricconstantwithsamesymb01.Thedi
7、fferenceofelasticmodulebetweencomponentsbroughttolooseconnectivitybetweenthem·Asto0-3typecomposite,thestressesdeliverthroughspacenetworkconstructedbythepolymer.Whereas,thewidegapmoduledelayedthoseinnerstressdelivering-Whilethestresseswerecutdowninceramicparticleswhichtookpartinthei
8、iiAbstradmostpiezoelectric