niti形状记忆合金增韧al2o3陶瓷的研究

《niti形状记忆合金增韧al2o3陶瓷的研究》由会员上传分享，免费在线阅读，更多相关内容在学术论文-天天文库。

1、山东人学硕士学位论文致密度，从而提高复合陶瓷的强度和韧性。研究结果表明：受到外力的作用时，复合陶瓷中的NiTi合金发生应力诱导相变，相变过程中产生的体积膨胀会消耗裂纹扩展的能量，抑制裂纹扩展并使裂纹发生偏转，提高复合陶瓷断裂韧性；同时NiTi合金颗粒的桥联作用可抑制裂纹的继续扩展，改善陶瓷韧性。关键词：A1203陶瓷；NiTi合金；增韧；复合陶瓷山尔大学硕十学位论文ABSTRACTCeramichashighstrength，highhardness，wearresistance，corrosionresistance，electricalinsulationfeatures，soit

2、iswidelyusedindailylife，industrialproductionandhigh·techfields，buttheroadblocktoitsapplicationispoorfracturetoughness．Therefore，howtoimproveceramictoughnessandpreparationhastheextremelyvitalsignificance．Overtheyears，thepeoplethroughvarioustougheningmethodstOimproveceramictoughness．Thecommontough

3、eningmethodshaveparticledispersiontoughening，fiberandwhiskertoughening，zirconiaphasetransformationtoughening，compositetougheningandself-toughening，etc．Atpresent，becauseNiTishapememoryalloywithrichphasetransitionphenomenon，SOitiswidelyusedinaerospace，architecture，biomedicalanddailylife，etc．Thispa

4、perselectsaluminaceramicsassubstrate，NiTialloyparticlesasthesecondphasecompositetoaluminaceramicsubstrate．ThroughtheNiTialloymartensitetransformationtoimprovethecharacteristicsofaluminaceramictoughness．Inthispaper，theeffectofNiTialloyonaluminaceramicflexuralstrengthandfracturetoughnessweretested

5、withaCMT5105Electromechanicaluniversaltestingmachine；AHD一1875hardnesstestingmachinewasemployedtotestthehardnessofthecompositeceramic；thispaperresearchedthephasecompositionofcomposite；byscanningelectronmicroscopetoobserveandanalyzethefracturemorphologyofceramicmaterials，anddiscussthetougheningmec

6、hanism．ThispaperpreparedamorphousNiTialloypowderbymechanicalalloying．Afterthecrystallizationprocessing，madethealloydispersedhomogeneouslytoaluminasubstrate．Under14000Cand13000Csinteringtemperaturepreparedcompositeceramicbyhot—presssinteringprocess．MeanwhilethispapermadeequiatomicNiTialloycomposi

7、tedtoaluminasubstrate，under1300。Csinteringtemperaturepreparedcomposites．Inthemeantime，thispapercontrastedtheirmechanicalpropertytothecompositeceramicswhichweFccompositedNiTialloybymechanicalalloying．Theresultindicatesthatmec