1、第43卷,第5期工程塑料应用V0l43,N。~492015年5月ENGINEER1NGPLASTICSAPPLICATIONMay2015。doi:lO.3969~.issn.1001-3539.2015.05.010熔体拉伸PE-HD和PE-LLD薄膜的制备及性能吴芬,闫学增,王静静。林文松,邹义冬(1.上海丁程技术大学材料工程学院,上海201620;2.上海材料研究所,上海市工程材料应用评价重点实验室,上海200437;3.东华理工大学化学生物与材料科学学院,南昌330013)摘要:以高密度聚乙烯(PE-HD)和线型低密度聚乙
2、烯(PE-LLD)树脂为原料,采用转矩流变仪,借助熔体拉伸法制备了具有取向结构的PE-HD膜和PE-LLD膜。利用偏光显微镜、傅立叶变换红外光谱、差示扫描量热、小角激光散射及力学性能测试分析不同熔体拉伸速率下PE-HD膜和PE-LLD膜的结构与性能变化情况。结果表明,熔体拉伸速率越高,PE-HD膜和PE-LLD膜的相对取向度越高,快速拉伸PE-HD膜和PE—LLD膜的相对取向度分别为2.043和1.556;熔体拉伸速率对PE-HD膜和PE-LLD膜的结晶温度影响不大,两种膜具有显著的结晶性,PE-HD膜的结晶性更好;随熔体拉伸速率
3、的提高,PE-HD膜和PE-LLD膜的拉伸屈服应力和拉伸弹性模量提高,断裂伸长率降低,总体上看,PE-LLD膜的断裂伸长率较PE—HD膜高,而拉伸强度较PE—HD膜低。关键词:聚乙烯;熔体拉伸;取向度;结晶;力学性能中图分类号:TQ321.5文献标识码:A文章编号:1001.3539(2015)05.0049.05PreparationandPropertiesofMeltStretchingPE-HDandPE-LLDFilmsWuFen一,YanXuezeng,WangJingjing,LinWensong,ZouYidong
4、f1.CollegeofMaterialsEngineering,ShanghaiUniversityofEngineeringScience,Shanghai201620,China;2.ShanghaiKeyLaboratoryofEngineeringMaterialsApplicationandEvaluation,ShanghaiResearchInstituteofMaterials,Shanghai200437,China;3.SchoolofChemistryBiologyandMaterialScience,Ea
5、stChinaInstituteofTechnology,Nanchang330013,China1Abstract:Usinghighdensitypolyethylene(PE—HD)andlinearlowdensitypolyethylene(PE-LLD)resinasrawmaterials,thePE-HDandPE-LLDfilmswithorientationstructurewerepreparedbythemeltstretchingmethodwithtorquerheometer.Thevariation
6、sofstructureandpropertiesofthePE—HDandPE-LLDfilmsindiferentmeltstretchingrateswerestudiedbypolarizationmicroscopic,FTIR,DSC,SALSandmechanicalprope~iestest.Theresultsshowthatwhenthemeltstretchingrateisfaster,theorientationdegreesofthefilmsarehigher,andtherelativeorient
7、ationdegreeofrapidstretchingPE-HDandPE-LLDfilmsis2.043and1.556respectively.Meltstretchingratehasslightefectsonthecrystallizationtemperatureofthefilms,thetwokindsoffilmshaveobviouscrystallinity,butthecrystallinityofthePE-HDfilmisbetter.Withtheincreaseofmeltstretchingra
8、te,thetensilestressatyieldandmodulusofelasticityintensionofthePE-HDandPE-LLDfilmsareimproved,butelongationatbreakisdecreased