1、高温合金木身具备耐高温、耐腐蚀等优良性能,但是由于其使用环境复杂、严苛,在使用过程中也会发生疲劳、高温蠕变、变形等,为了进一步提升高温合金表面硕度及耐蚀性等要求,尝试使用化学复合镀的手段强化合金表面。在高温合金表面制备了一种Ni-P-Al2O3复合镀层。使用单因素手段研究了纳米AI2O3颗粒的分散方式、添加量、搅拌速率以及时间对镀层显微硕度的影响。结果表明:使用酒精分散可以使颗粒在镀层屮呈现弥散分布;当颗粒浓度在O.5g/L〜9g/L范围内逐渐增加时,镀层硕度先增加后减小,在lg/L时达到最大值;当搅拌速率逐渐增大时,镀层硬度逐渐降低,100r/min的硕度最大;镀层硕度
2、随时间增大先升高后减小,当时间为lh时,得到的镀层硕度值最大。当颗粒添加量为lg/L,搅拌速率为lOOr/min,复合镀时间为lh时制备的镀层硬度最大,达到609.18Hvo研究了镀层的热性能,镀层在400°C热处理lh后呈现出最好的性能,硕度达930.92Hvo关键词:高温合金;化学复合镀;硬度;工艺;热处理AbstractSuperalloyhashightemperatureresistance,corrosionresistance,excellentperformance,butbecauseofitsapplicationofenvironmentiscomp
3、lex,demanding,itwilloccur,hightemperaturecreepdeformation,etc.,inordertofurtherimprovethehigh-temperaturealloysurfacehardnessandcorrosionresistanceetc,whenused.wetryusingcompositeplatingmeansofstrengtheningthealloysurface.Inthehigh-temperaturealloyplatedaNi・P・AI2O3compositecoating.Theeffe
4、ctoftheconcentrationsofnano-ALOs,dispersionmethods,stirringspeedandcompositeplatingtimeonthemicrohardnessofelectrolesscompositecoatingswasinvestigatedbysinglefactorexperiment.Theresultsindicatethatparticlesdispersedinthecoatingpresented,whenusingalcoholdispersion,Coatinghardnessdecreasesa
5、fterthefirstincreaseandreachingamaximumatlg/L,Whentheparticleconcentrationisgraduallyincreasedduring0.5g/L-9g/L;coatinghardnessdecreased,thehardnessmaximumis100r/min,whenthestirringspeedisgraduallyincreased;thecoatinghardnessdecreaseswithtimeafterthefirstrise.whenthetimeislh,coatinghardne
6、ssismaximum.Thecompositeplatinghasgoodproperties,compositeplatingmicrohardnessis609.18HVwhenthenano-AhOsparticlesisalcoholicwetting,theconcentrationofAI2O3islg/L,thestirringspeedis100r/min,thetimeofcompositeplatingislh.Thethermalpropertiesofthecoatingin400°Cxlhheattreatment5theelectroless
7、compositeplatingmicrohardnessisupto930.92Hv.Keyword:superalloy;chemicalplating;chemicalcompositeplating;microhardness;corrosionresistance目录摘要IAbstractII第一章绪论11.1咼温合金11.1.1高温合金简介11.1.2高温合金按照基体元素分类11.1.3高温合金的应用21.2化学镀发展及研究现状21.2.1化学镀的概述21.2.2Ni・P化学镀的工艺条件31.2.3化学镀Ni・P的