不同牌号碳钢的化学成分表

《不同牌号碳钢的化学成分表》由会员上传分享，免费在线阅读，更多相关内容在应用文档-天天文库。

1、不同牌号碳结钢的化学成分表序号统一数字代号牌号化学成分.%CSiMnCrNiCu不大于1U2008008F0.05～O.11≤0.030.25～0.500.100.300.252U2010010FO.07～0.13≤0.07O.25～0.500.150.300.253U2015015F0.12～0.18≤0.07O.25～0.500.25O.300.254U20082080.05～0.110.17～0.37O.35～0.650.10O.300.255U2010210O.07～O.130.17～0.37O.35～0.65O.15O.300.256U20152150.12～0.18O.17～0.3

2、70.35～0.65O.25O.300.257U20202200.17～0.230.17～0.37O.35～0.65O.25O.300.258U2025225O.22～0.29O.17～0.370.50～0.80O.250.300.259U20302300.27～0.340.17～0.37O.50～0.80O.25O.300.2510U20352350.32～0.39O.17～0.370.50～0.80O.25O.300.2511U20402400.37～0.44O.17～0.370.50～0.800.Z5O.300.2512U2045245O.42～O.50O.17～0.370.50～0.8

3、0O.25O.300.2513U2050250O.17～0.37O.50～0.80O.25O.300.25O.47～0.5514U2055255O.52～0.600.17～0.370.50～0.80O.250.300.2515U2060260O.57～0.650.17～0.370.50～0.800.25O.300.2516U20652650.62～0.70O.17～0.370.50～0.80O.25O.300.2517U2070270O.67～0.75O.17～0.370.50～0.800.250.300.2518U2075275O.72～0.800.17～0.370.50～0.80O.250

4、.300.2519U2080280O.77～0.85O.17～0.370.50～0.800.250.300.2520U2085285O.82～0.900.17～0.370.50～0.800.25O.300.2521U2115215MnO.12～0.180.17～0.37O.70～1.000.25O.300.2522U2120220Mn0.17～0.230.17～0.370.70～I.000.25O.300.2523U2125225Mn0.22～0.290.17～0.37O.70～1.00O.25O.300.2524U2130230MnO.27～0.340.17～0.37O.70～1.00O.2

5、5O.300.2525U2135235M13O.32～0.390.17～0.37O.70～1.00O.250.300.2526U2140240M13O.37～0.440.17～0.370.70～1.000.25O.300.2527U2145245MnO.42～0.50O.17～0.37O.70～1.000.25O.300.2528U2150250Mn0.48～0.560.17～0.37O.70～1.00O.25O.300.2529U2160260Mn0.57～O，650.17～0,37O.70～1.00O.25O.300.2530U2165265M13O.62～0.700.17～0.37O.9

6、0～1.20O.25O.300.2531U2170270M130.67～0.750.17～0.37O.90～1.20O.25O.300.25注：表1所列牌号为优质钢。如果是高级优质钢，在牌号后面加“A”(统一数字代号最后一位数字改为“3”)；如果是特级优质钢，在牌号后面加。E”(统一数字代号最后一位数字改为“6”)；对于沸腾钢，牌号后面为“F”(统一数字代号最后一位数字为“0”)；对于半镇静钢，牌号后面为“b”(统一数字代号最后～位数字为“1”)