1、学兔兔www.xuetutu.com2014年第3期(总第293期)混凝土理论研究Number3in2014(TotalNo.293)ConcreteTHEORETICALRESEARCHdoi:10.3969~.issn.1002—3550.2014.03.001胶凝材料组成对高强混凝土早期温升的影响崔强。王栋民’,阎培渝(1.中国矿业大学(JL京)化学与环境工程学院,北京100083;2.清华大学土木系,北京100084)摘要:分别在25、5O℃条件下测定了水泥、水泥一矿渣、水泥一粉煤灰一硅灰三种不同胶凝材料的水化放热特性,并测定了分别用三种胶凝材料配制的相同强度等级的混凝土的绝热
2、温升。试验结果表明:无论在常温还是高温条件下,水泥一粉煤灰一硅灰体系的水化放热速率始终低于纯水泥体系;水泥一矿渣体系的水化放热速率在水化减速期的后阶段超过纯水泥体系,使其与纯水泥体系的放热量差距缩小;提高水化温度对水泥一矿渣体系的水化促进作用非常明显。混凝土的初期绝热温升与其胶凝材料在常温条件下的水化放热特性相关性强,随着内部温度的增大,绝热温升与其胶凝材料在高温条件下的水化特性具有更好的相关性。关键词:粒化高炉矿渣;粉煤灰;硅灰;绝热温升;水化热中图分类号:TU528.O1文献标志码:A文章编号:1002—3550(2014)03—0001—03Influenceofcementit
3、iousmaterialcompositionontheearlytemperatureriseofhighstrengthconcreteC叫(~ang,WANGDongmin,YANPeiyu(1.SchoolofChemicalandEnvironmentalEngineering,ChinaUniversityofMiningandTechnology,Beijing100083,China;2.DepartmentofCivilEngineering,TsinghuaUniversity,Beijing100084,China)Abstract:Theexothermicpr
4、opertiesofcement,cement-ggbs,cement—flyash—silicafumeweredeterminedundertheconditionsof25℃and50℃.respectively.Inthemeanwhile,theadiabatictemperaturerisesoftheconcretespreparedbythethreebinderswiththesamestrengthgradeweredetermined.Theresultsshowthattheexothermicrateofcement-flyash—silicafumeislo
5、werthanthatofpurecementateachperiodunderwhether25℃or50℃.Theexothermicrateofcement—ggbsexceedsthatofpurecementatthelatedecelerationperiod.whichdecreasesthedifferenceofhydrationheatbetweenthetwocementitioussystems.Theinfluenceofincreasinghydrationtemperatureonthehydrationofcement·ggbsisthemostsign
6、ificant.Thedisciplineoftheinitialadiabatictemperaturerisesofconcretesandtheircemen—titiousmaterialsexothermicpropertiesundernormaltemperatureconditionshaveastrongcorrelation.Asthetemperaturerisesinsidetheconcretes,thedisciplineoftheadiabatictemperaturerisesandtheircementitiousmaterialsexothermic
7、prope~iesunderhightemperatureconditionshaveabettercorrelation.Keywords:granulatedblastfurnaceslag;flyash;silicafume;adiabatictemperaturerise;hydrationheat注的,因为这与影响高强混凝土早期体积稳定性的很多因0引言素密切相关。本试验选择了工程上常用的矿渣、粉煤灰和硅胶凝材料用量大是高强混凝土材料组