热电偶温度对照表

《热电偶温度对照表》由会员上传分享，免费在线阅读，更多相关内容在应用文档-天天文库。

1、铂铑10--铂热电偶分度表分度号S(参考端温度为0℃)───┬────────────────────────────────────────────温度│热电动势(mV)├────────────────────────────────────────────℃│0123456789───┴────────────────────────────────────────────-50-0.236-40-0.194-0.199-0.203-0.207-0.211-0.215-0.220-0.224-0.228-0.232-30-0.150-0.1

2、55-0.159-0.164-0.168-0.173-0.177-0.181-0.186-0.190-20-0.103-0.108-0.112-0.117-0.122-0.127-0.132-0.136-0.141-0.145-10-0.053-0.058-0.063-0.068-0.073-0.078-0.083-0.088-0.093-0.098-00-0.005-0.011-0.016-0.021-0.027-0.032-0.037-0.042-0.048000.0050.0110.0160.0220.0270.0330.0380.0440

3、.050100.0550.0610.0670.0720.0780.0840.0900.0950.1010.107200.1130.1190.1250.1310.1370.1420.1480.1540.1610.167300.1730.1790.1850.1910.1970.2030.2100.2160.2220.228400.2350.2410.2470.2540.2600.2660.2730.2790.2360.292────────────────────────────────────────────────续分度号S续表1───┬────

4、────────────────────────────────────────温度│热电动势(mV)├────────────────────────────────────────────℃│0123456789───┴────────────────────────────────────────────500.2990.3050.3120.3180.3250.3310.3380.3450.3510.358600.3650.3710.3780.3850.3910.3980.4050.4120.4190.425700.4320.4390.44

5、60.4530.4600.4670.4740.4810.4880.495800.5020.5090.5160.5230.5300.5370.5440.5510.5580.566900.5730.5800.5870.5940.6020.6090.6160.6230.6310.6381000.6450.6530.6600.6670.6750.6820.6900.6970.7040.7121100.7190.7270.7340.7420.7490.7570.7640.7720.7800.7871200.7950.8020.8110.8180.8250.

6、8330.8410.8480.8560.8641300.8720.8790.8870.8950.9030.9100.9180.9260.9340.9421400.9500.9570.9650.9730.9810.9890.9971.0051.0131.0211501.0291.0371.0451.0531.0611.0691.0771.0851.0931.1011601.1091.1171.1251.1331.1411.1491.1581.1661.1741.1821701.1901.1981.2071.2151.2231.2311.2401.2

7、481.2561.2641801.2731.2811.2891.2971.3061.3141.3221.3311.3391.3471901.3561.3641.3731.3811.3891.3981.4061.4151.4231.432────────────────────────────────────────────────续分度号S续表2───┬────────────────────────────────────────────温度│热电动势(mV)├──────────────────────────────────────────

8、──℃│0123456789───┴────────────────────────────────────────────2001.4