《镍钨合金镀层的制备及性能研究》由会员上传分享,免费在线阅读,更多相关内容在学术论文-天天文库。
1、摘要化学镀Ni-W-P镀层具备硬度高、镀层厚度均匀、耐蚀性且耐磨性好等优势,于是,制备优质的镍钨合金镀层近年来成为世界各国的钻研的热门。实验采用化学镀法制备了Ni-W-P合金镀层,用SEM、XRD、电化学、点滴实验、硬度等测试手段对其性能进行表征。在钢铁表面制备了Ni-W-P合金镀层。研究了钨酸钠、硫酸镍、次磷酸钠、乳酸、温度等工艺参数对化学镀镍层沉积速度、点滴时间、电化学性能等的影响,–1通过正交实验优化出了化学镀Ni-W-P合金镀层的较佳工艺配方:35g·L硫酸镍,–1–1–1–1–115g·L钨酸钠,35g·L次亚磷酸钠,30g·L硫酸铵,32g
2、·L柠檬酸钠,8g·L–1–1–1苹果酸,15ml·L乳酸,2-5mg·L碘酸钾,1mg·L硫脲,镀液pH值为4.8-5.1,温度为88℃。制备的Ni-W-P合金镀层结构呈现典型的高磷非晶态,其磷含量达11.1%。Ni-W-P合金镀层点滴时间为70s,耐蚀性略低于Ni-P镀层的76s,但其硬度为679.18HV,较镍磷合金镀层(562.14HV)和基体(268.1HV)分别提高了约117.04HV和411.08HV。结合力测试结果发现Ni-W-P合金镀层的结合力强于Ni-P镀层。对制备的Ni-W-P合金镀层进行热处理。研究了200—800℃下热处理对镀
3、层性能的影响,结果表明随着热处理温度的升高,镀层由非晶态逐步转化成为晶态,硬度呈现先增大后减小的趋势。当温度达到400℃时,衍射峰增强,镀层的胞状物边缘变得模糊,镀层的硬度值最大为1070.1HV,磨损量最小为5.3mg。化学镀Ni-W-P合金镀液的使用寿命。采用补加方法测出镀液的循环寿命为-15MTO,在使用周期内镀液的沉积速度稳定在11µm·h以上,镀态硬度在670HV左右。关键词:化学镀;Ni-W-P镀层;镀速;耐蚀性ABSTRACTElectrolessNi-W-Palloyplatingshavemanyadvantagessuchasgoo
4、dwearresistance,corrosionresistance,filmthicknessuniformity,highhardnessandsoon.Andhence,preparinggoodperformanceofNi-W-Palloycoatingbecomesahottopicinrecentyearsathomeandabroad.Inthisexperiment,theperformancesofNi-W-Palloycoatingpreparedonstainlesssteelsubstratehavebeentestedby
5、aseriesofmethodssuchasdriptest,thedepositionrate,micro-hardness,electrochemistry,scanningelectronmicroscopyandsoon.ElectrolessNi-W-Palloycoatingswerepreparedonstainlesssteel.Thesodiumtungstate,nickelsulfate,sodiumhypophosphite,lacticacid,temperatureandotherprocessparametersweres
6、tudiedonthedepositionrateofelectrolessnickelplatinglayer,theinfluenceofthebittime,theelectrochemicalproperties,etc.Theoptimumformulaacquiredbycombingwiththesinglefactorandorthogonalexperimentmethod-1-1areasfollowing:nickelsulfate35g·L,sodiumtungstate15g·L,hypophosphite-1-1-1-135
7、g·L,ammoniumsulfate30g·L,sodiumcitrate32g·L,malicacid8g·L,lactic-1-1-1acid15ml·L,potassiumiodate2-5mg·L,thiourea1mg·L,pH4.8to5.1,temperature88℃,time1.5h.ThestructureofNi-W-PalloyplatingistypicalcrystallinestatewithhighcontentofPelement(11.9%).Theresultsshowedthatthecorrosionrisi
8、stanceofNi-W-Palloyplating(driptime70s)isnearly