抗穿刺线型低密度聚乙烯薄膜的制备

《抗穿刺线型低密度聚乙烯薄膜的制备》由会员上传分享，免费在线阅读，更多相关内容在学术论文-天天文库。

1、·566·PETROCHEMICALTECHNOLOGY2014年第43卷第5期抗穿刺线型低密度聚乙烯薄膜的制备蔡传伦，张晓红，赖金梅，高建明，王亚，宋志海（中国石化北京化工研究院，北京100013）［摘要］采用γ射线对线型低密度聚乙烯（LLDPE）进行辐照得到辐照LLDPE（xPE）。用xPE和茂金属LLDPE（mPE）分别与LLDPE共混改性制得抗穿刺LLDPE/xPE和LLDPE/mPE薄膜。利用DSC，GPC，SEM等方法分析了上述3种薄膜的抗穿刺性能。实验结果表明，对于LLDPE/xPE

2、薄膜，随xPE用量的增大，抗穿刺性能增强，当m（LLDPE）∶m（xPE）=80∶20时，抗穿刺力为14.4N，较LLDPE薄膜提高了15.2%；抗穿刺能为268.0mJ，较LLDPE薄膜提高了24.9%。对于LLDPE/mPE薄膜，当m（LLDPE）∶m（mPE）=90∶10时，抗穿刺力为14.5N，较LLDPE薄膜提高约16.0%；抗穿刺能为288.7mJ，较LLDPE薄膜提高了34.5%。xPE和mPE中含有的少量长支链有利于增强分子链间的缠结，提高分子链间相互作用力，从而改善LLDPE薄膜的抗

3、穿刺性能，延长薄膜使用寿命。［关键词］抗穿刺性能；线型低密度聚乙烯；共混改性；薄膜PreparationandCharacterizationofPuncture-ResistantLinearLowDensityPolyethyleneFilm［文章编号］1000-8144（2014）05-0566-05［中图分类号］TQ322.2［文献标志码］ACaiChuanlun，ZhangXiaohong，LaiJinmei，GaoJianming，WangYa，SongZhihai（SINOPECBeij

4、ingResearchInstituteofChemicalIndustry，Beijing100013，China）［Abstract］Linearlowdensitypolyethylene(LLDPE)wastreatedwithγ-rayradiationtoprepareirradiatedLLDPE(xPE).Puncture-resistantLLDPE/xPEandLLDPE/mPE(mPE：LLDPEpreparedwithmetallocenecatalyst)filmswerep

5、reparedbyblendingLLDPEwithxPEandmPE，respectively.PuncturepropertiesofthefilmswereinvestigatedbymeansofDSC，GPCandSEM.TheresultsshowedthatthepuncturepropertiesofLLDPE/xPEfilmincreasedwithincreasingxPEdosage.Attheratioofm(LLDPE)∶m(xPE)as80∶20，thepuncturefo

6、rceandpunctureenergyofthefilmwere14.4Nand268.0mJ，increasingby15.2%and24.9%comparedtotheLLDPEfilm，respectively.ThepunctureforceandpunctureenergyofLLDPE/mPEfilmattheratioofm(LLDPE)∶m(mPE)as90∶10were14.5Nand288.7mJ，increasingby16.0%and34.5%comparedtotheLLD

7、PEfilm，respectively.TheimprovementofthepuncturepropertiesofthefilmsmaybeduetothesmallamountoflongchainbranchinginxPEandmPE，whichcansignificantlyenhancethechainentanglementandtheinteractionbetweenLLDPEchains.SotheusefullifeoftheLLDPEfilmscanbeprolonged.［

8、Keywords］punctureresistance；linearlowdensitypolyethylene；blendingmodification；film线型低密度聚乙烯（LLDPE）是以乙烯与α-烯烃（如1-丁烯）共聚得到的聚乙烯树脂，其密度范围为0.910～0.940g/cm3［1］。LLDPE薄膜的综合性能优异，具有良好的拉伸和撕裂强度，且耐寒、耐候性较好，是适合不同地区气候条件被广泛使用的通用薄膜（如农膜、棚地膜等）材料。LLDPE的分